Comparison of a Nanofiber-Reinforced Composite with Different Types of Composite Resins

Özduman Z. C., Oglakci B., Bagis D. M. H., Temel B., Dalkilic E.

Polymers, cilt.15, sa.17, 2023 (SCI-Expanded, Scopus) identifier identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 15 Sayı: 17
  • Basım Tarihi: 2023
  • Doi Numarası: 10.3390/polym15173628
  • Dergi Adı: Polymers
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Academic Search Premier, Aerospace Database, Chemical Abstracts Core, Communication Abstracts, Compendex, Food Science & Technology Abstracts, INSPEC, Metadex, Directory of Open Access Journals, Civil Engineering Abstracts
  • Anahtar Kelimeler: composite, fiber, mechanical, nano, physical properties, polymer
  • Bezmiâlem Vakıf Üniversitesi Adresli: Evet

Özet

The aim of this study was a comprehensive evaluation and comparison of the physical and mechanical properties of a newly developed nano-sized hydroxyapatite fiber-reinforced composite with other fiber-reinforced and particle-filled composites. Commercially available eight composite resins (3 fiber-reinforced and 5 particle-filled) were used: Fiber-reinforced composites: (1) NovaPro Fill (Nanova): newly developed nano-sized hydroxyapatite fiber-reinforced composite (nHAFC-NF); (2) Alert (Pentron): micrometer-scale glass fiber-reinforced composite (µmGFC-AL); (3) Ever X Posterior (GC Corp): millimeter-scale glass fiber-reinforced composite (mmGFC-EX); Particle-filled composites: (4) SDR Plus (Dentsply) low-viscosity bulk-fill (LVBF-SDR); (5) Estelite Bulk Fill (Tokuyama Corp.) low-viscosity bulk-fill (LVBF-EBF); (6) Filtek Bulk Fill Flow (3M ESPE) low-viscosity bulk-fill (LVBF-FBFF); (7) Filtek Bulk Fill (3M ESPE) high-viscosity bulk-fill (HVBF-FBF); and (8) Filtek Z250 (3M ESPE): microhybrid composite (µH-FZ). For Vickers microhardness, cylindrical-shaped specimens (diameter: 4 mm, height: 2 mm) were fabricated (n = 10). For the three-point bending test, bar-shaped (2 × 2 × 25 mm) specimens were fabricated (n = 10). Flexural strength and modulus elasticity were calculated. AcuVol, a video image device, was used for volumetric polymerization shrinkage (VPS) evaluations (n = 6). The polymerization degree of conversion (DC) was measured on the top and bottom surfaces with Fourier Transform Near-Infrared Spectroscopy (FTIR; n = 5). The data were statistically analyzed using one-way ANOVA, Tukey HSD, Welsch ANOVA, and Games–Howell tests (p < 0.05). Pearson coefficient correlation was used to determine the linear correlation. Group µH-FZ displayed the highest microhardness, flexural strength, and modulus elasticity, while Group HVBF-FBF exhibited significantly lower VPS than other composites. When comparing the fiber-reinforced composites, Group mmGFC-EX showed significantly higher microhardness, flexural strength, modulus elasticity, and lower VPS than Group nHAFC-NF but similar DC. A strong correlation was determined between microhardness, VPS and inorganic filler by wt% and vol% (r = 0.572–0.877). Fiber type and length could affect the physical and mechanical properties of fibers containing composite resins.